Method and apparatus for reducing particulate iron oxide to metallic iron with solid reductant

ABSTRACT

A method and apparatus for reducing particulate iron oxide to metallic iron utilizing solid carbonaceous fuel as reductant in a shaft type reducing furnace, in which a furnace burden is formed of a mixture of iron oxide lumps or pellets and particulate solid fuel. Reacted top gas is upgraded and recirculated through the burden in counter-flow relationship thereby heating and partially reducing the burden. The heat for final reduction is generated by passing electric current through the burden.

This is a division of application Ser. No. 769,242, filed Feb. 16, 1977 now U.S. Pat. No. 4,082,543.

BACKGROUND OF THE INVENTION

In recent years the direct reduction of iron oxide to metallic iron has become a practical commercial reality with increasing worldwide acceptance and production. The direct reduced iron which results from direct reduction of iron oxide has a commercially demonstrated utility in iron and steelmaking and particularly in electric arc furnace steelmaking. The world demand today for direct reduced iron far exceeds the production capability of existing and planned direct reduction plants, due primarily to the dependence upon natural gas as the energy source in most of the direct reduction processes which have been commercially developed.

To satisfy the short-term and long-term demand for direct reduced iron, it is essential that new and improved direct reduction processes utilize solid fuels such as coal or lignite, to make direct reduction practical in those many countries such as the United States where large reserves of solid fuels are available and natural gas reserves are limited.

In recent efforts to develop direct reduction processes which utilize solid fuels as the source of reductant for the reduction process have been directed primarily to two different basic types of processes. One type of process mixes solid fuel with iron oxide and processes the mixture in a rotary kiln, using air for combustion in the kiln. A typical example of this process is described in U.S. Pat. No. 3,046,106. The rotary kiln process has a fundamental thermal disadvantage in that approximately 65% of the solid fuel consumed by combustion is required to maintain the high temperature of the kiln, and only about 35% of the fuel value is available for reduction. This results in a solid fuel requirement in the range of 5.0 to 6.0 Giga calories per metric ton of direct reduced iron product.

A second type process gasifies the solid fuel in a separate combustion-type gasifier utilizing oxygen and steam for the gasification. The gas from the gasifer is then cooled and scrubbed, desulfurized, then utilized in a direct reduction furnace as the source of reductant. An example of this combination of gasifier and direct reduction furnace is described in U.S. Pat. No. 3,844,766. This combination also has a fundamental thermal disadvantage in that approximately 50% of the solid fuel is consumed by combustion in the gasifier and only the remaining 50% of the fuel value is available as a source of reductant. This combination, although highly efficient in the use of the gas from the gasifier for reduction, requires approximately 4.0 to 5.0 Giga calories of solid fuel per metric ton of direct reduced iron.

In both types of solid fuel direct reduction processes described above, a major portion of the fuel value of the solid fuel is consumed by oxygen from air or from industrial oxygen. In the rotary kiln, only a minor portion is consumed by reaction with oxygen from the iron oxide being reduced.

French Pat. No. 2,274,694 discloses a shaft furnace having a tubular reaction chamber through which the burden passes. The tube is externally heated by burners. The charge to the furnace is iron ore and coke with an optional desulphurizing agent. No provision is made handling the products of reaction nor for utilizing them in the process. The external heating of the tube of this type furnace creates a temperature gradient in the burden because the burden is not a good conductor of heat.

An electrically operated vertical shaft furnace is taught by U.S. Pat. No 1,937,064 in which broken coke, graphite, silicon carbide or other conductors are charged to form a burden. Molten metal is then poured through the burden while electrical current also flows through the burden, thus refining the molten metal. The burden is a stationary granular mass of carbonaceous material which does not flow through the furnace. The burden also is not the material being treated, unlike the present invention.

Other patents which may be of interest to the reader include Carlsson U.S. Pat. No 2,089,782, Brugger U.S. Pat. No. 2,755,325 and Southam U.S. Pat. No. 3,161,500.

OBJECTS OF THE INVENTION

It is the principal object of the present invention to provide a method for directly reducing iron oxide to metallic iron in a shaft type reduction furnace wherein solid fuel is utilized as the reductant source.

It is another object of this invention to provide a method for directly reducing iron oxide in a shaft furnace wherein the energy input requirements are greatly reduced over present commercial direct reduction methods.

It is another object of this invention to provide means for more efficient operation of a direct reduction shaft furnace than was heretofore possible.

It is another object of this invention to provide apparatus for carrying out the above methods.

SUMMARY OF THE INVENTION

The present invention is directed to a direct reduction method utilizing solid fuel in a novel and highly thermally efficient manner wherein the solid fuel is consumed directly in the reduction process by reaction with oxygen from the iron oxide which is being reduced. The overall reactions in the furnace are endothermic, the heat required being supplied by electrically heating the burden. Exclusion of an external source of air or industrial oxygen results in a solid fuel requirement of approximately 2.2 Giga calories per metric ton of direct reduced iron product with an additional electric energy requirement of approximately 700 kwh (0.6 Giga calories) per metric ton of direct reduced iron.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

The present invention will be more readily understood by referring to the following detailed specification and the appended drawings in which:

FIG. 1 is a schematic cross section of an elevational view of the shaft furnace of the present invention showing gas flows and related equipment.

FIG. 2 is an elevational cross section of an alternative embodiment of the present invention.

FIG. 3 is an elevational cross section of another alternative embodiment of the present invention.

FIG. 4 is a schematic diagram showing vertically spaced electrodes as alternative means for providing electric heat to the shaft furnace burden.

FIG. 5 is a schematic cross-section of an elevational view of the furnace of FIG. 4 showing modifications to the electrodes.

FIG. 6 is a schematic cross section of an elevational view of the furnace of FIG. 5 taken through the line 6--6 of FIG. 5.

DETAILED DESCRIPTION

Referring now to the embodiment of FIG. 1, a shaft type furnace 10 having a steel shell 12 is lined with refractory 14. A feed hopper 16 is mounted at the top of furnace 10 for charging of particulate solids feed material 18 therein. The feed material consists of iron oxide in the form of pellets or lumps, and solid carbonaceous fuel. The feed material descends by gravity through one or more feed pipes 20 to form a packed bed 22 of particulate solids feed material or burden in the furnace 10. Reduced product is removed from the furnace by discharge conveyor 26 located beneath discharge pipe 24. Removal of the reduced product, which is in the form of metallized pellets or lumps from discharge pipe 24 establishes a gravitational flow of the particulate burden 22 through shaft furnace 10.

The furnace 10 is preferably square or rectangular in horizontal cross section. The middle region of the furnace is provided with heat resistant alloy electrode plates 30 connected to electrode lead rods 32, which are in turn connected to an electric power source not shown. Electrode plates 30 are preferably recessed into the refractory wall 14 to create a substantially smooth interior wall face. The electrode plates are so positioned to form opposing pairs. Three opposing pairs of electrode plates are shown in FIG. 1, vertically spaced through the furnace for reasons of process control. The electrode lead rods 32 are mounted on suitable electrical insulating material 34 such as asbestos board which serves to insulate the rod 32 from the steel furnace shell 12. A heat resistant alloy pipe 38 having a closed lower end extends vertically through the furnace roof and into the burden as far as the region of the lower most pair of electrode plates 30. Suitable thermocouples, not shown, are inserted into the thermocouple pipe 38 to sense the temperature of the burden at selected elevations, particularly at the elevation of each pair of electrode plates.

Top gas exits the furnace through a top gas outlet pipe 44 located above stock line 46. The lower end of feed pipe 20 extends below outlet pipe 44, which arrangement creates a top gas disengaging plenum 48 which permits the top gas to exit generally symmetrically from the stock line 46 and flow freely to the top gas outlet pipe 44.

A gas cleaning and recirculating circuit is provided to remove solids and condensible matter from the top gas and to cool the gas to form cold process gas. The reacted top gas leaving the shaft furnace 10 through pipe 44 flows to an oil scrubber 50 wherein tars, oils, and particulates are removed from the gas as a sludge. Pump 52 pumps the sludge back through the furnace through sludge injection pipe 54 which has an open lower end extending well beneath the stock line to insure reaction of sludge components with the burden to prevent top gas from recycling these components back into the oil scrubber.

The top gas passes from the oil scrubber to a water scrubber 60 wherein the gas is further cooled and cleaned. A gas recirculating blower 62 draws the cooled and cleaned process gas from the scrubber 60. A valve 65 is provided in pipe 66 as required. A portion of the process gas is introduced to pipe 68 to assist in injecting the sludge into the shaft furnace burden. The major portion of the process gas is reintroduced to the furnace as cold process gas through gas inlet pipe 40 through a gas distributing member 42 located within the furnace. Some process gas must normally be vented because when solid carbon in the furnace reacts with oxygen from the iron oxide, carbon monoxide gas and carbon dioxide gas are formed. Since this reaction involves a gaseous expansion, excess gas may be vented through vent V. Of course, this excess gas provides a source of energy for use elsewhere.

An alternative embodiment of the invention depicted in FIG. 2 includes provision for introducing both cold process gas and hot process gas into the lower region of the furnace beneath the electrodes. Cold process gas is introduced through the cold process gas inlet pipe 40 in the ame manner as the embodiment of FIG. 1. Hot process gas is introduced to the burden through hot process gas inlet pipe 72 and gas distributing member 74 located within the furnace. The region between the cold process gas distributing member and the hot process gas distributing member acts as a cooling zone to cool the hot product prior to discharge.

The top gas leaves the burden at the stock line and exits the furnace through top gas takeoff pipe 44. The top gas is cleaned of tars, oils, and particulates in oil scrubber 50, then further cleaned and cooled in water scrubber 60. A portion of the process gas is reintroduced to the furnace as cold process gas through process gas inlet 40. A second portion of the process gas passes through pipe 79 into gas preheater 80. The heated gas flows through pipe 82 and is introduced to the furnace through hot process gas inlet 72. A third portion of cold process gas is directed through pipe 84 and is injected into sludge return line 86 to assist in carrying the sludge back to the furnace. Another portion of the process gas is fed into pipe 88 as fuel for preheater burner 90. A vent V₁, is provided in pipe 88 to vent a portion of the cooled process gas, as required. Combustion air for the burner 90 is provided by air source 92. Vent V₂ removes the products of combustion from preheater 80.

The embodiment of FIG. 3 includes a cooling zone in the lower portion of the furnace whereby cooling gas is admitted to the furnace through cooling gas inlet 100 and cooling gas distributor 102 within the furnace. A cooling gas collecting member 104, which is positioned above gas distributing member 102 communicates with scrubber-cooler 108 through cooling gas outlet 110 and pipe 112. A recirculating gas blower 114 is positioned in pipe 116 or any other convenient location within the cooling gas circuit to provide the inpetus for gas flow. The cooling gas circuit includes the cooling zone of the furnace which is that portion of the furnace between the cooling gas distributing member 102 and the cooling gas collecting member 104.

In this FIG. 3 embodiment, only preheated process gas is introduced to the process gas inlet pipe 72. The remainder of the apparatus of FIG. 3 approximates that of FIG. 2.

An alternative arrangement for applying the electric power through the burden in a vertical direction is depicted in FIG. 4 wherein heat resistant alloy electrodes consisting of rods 126 and 127, one only of each being shown, extend through one wall of the casing 12 and across the furnace width terminating in the refractory wall on the opposite side of the furnace. Electrodes are provided at the upper and lower regions of the furnace as indicated in the drawing. Each rod may be equipped with heat resistant alloy discs 130 to provide an extended electrode surface area. The number of electrode rods employed is dependent upon the horizontal dimension of the furnace. When the electrodes are arranged to pass current vertically as depicted in FIG. 4, the furnace can have any desired cross-section including nearly every geometric shape such as square, round, rectangular, oval, etc.

Burden thermocouples 132 extend into the furnace at selected location heights through the sidewalls and are seated in electrical insulators 134 which engage the furnace casing 12. These thermocouples sense the temperature of the burden at the various locations as the burden passes through the furnace.

In the embodiment of FIG. 5, which is an alternative arrangement to that of FIG. 4, upper electrode 140 is journaled for rotation in bearings 142a and 142b which may be mounted externally as shown or insulated and mounted in the furnace walls 144.

One or more of these upper electrodes are provided, depending upon the dimensions of the horizontal cross-section of the furnace. The upper electrode acts as a feeder mechanism as well as a cluster breaker for material in the upper zone of the furnace. The electrode carries one or more radially extending breaker segments 146, best shown in FIG. 6. Upper electrode 140 is connected to and driven by oscillatible drive mechanism 148. At least one lower electrode 150 is provided which is journaled for rotation in insulated and sealed bearings 152a and 152b. These bearings may be in the walls of the furnace or mounted externally. Lower electrode 150 is connected to and driven by oscillatible drive mechanism 156. The lower electrode carries one or more radially extending arcuate breaker segments 158 and thus acts as a lower cluster breaker. Each cluster breaker segment extends only about 180° to 270° about the electrode. Thus as the electrode oscillates within the bearings, it acts as both a feed mechanism and cluster breaker mechanism. It feeds material alternately by moving material downwardly from opposite walls of the furnace while simultaneously breaking any clusters of the hot cohesive material.

In the method of this invention, iron oxide pellets, lump ore or other suitable iron oxide feed material is mixed with solid carbonaceous fuel such as coal, coke, or lignite, then fed through feed pipe 20 to the interior of the furnace 10 to form burden 22 therein as a packed bed.

The furnace is heated electro-thermally by passing electric current through the burden between alloy electrodes in the furnace. Directly reduced iron pellets or lumps are electrically conductive even at the earliest stage of reduction when metallatic iron is formed only on the pellet surface. When starting up operation of the electric powered shaft furnace of the present invention, the furnace is charged with partially metallized directly reduced iron pellets, petroleum coke or any other electrically conductive material. After a plant has been operating, reduced or partially metallized pellets would be readily available for a startup charge. However, other conductive materials are utilized when reduced or partially metallized pellets are unavailable. It has been determined that pellets with metallization as low as 6% are conductive.

The shaft furnac e includes three distinct process zones. The upper region constitutes a prereduction zone in which the burden is heated by convection of gases moving in counter-flow relation to the flow of the burden. Coal or other carbonaceous fuel in the feed liberates condensible and noncondensible volatiles. The noncondensible volatiles, which are mostly hydrogen or hydrocarbons, exit as top gas, are cleaned and recirculated as process gas. The pellet burden acts as a moving packed bed pebble quench which is very effective in preventing heavy liquid compounds from plugging gas outlet pipes. Some heavy oils and tars tend to weep out of the coal and are absorbed by the oxide feed to subsequently react with the CO₂ and water vapor in the process gas. A high ratio of oxide feed to heavy liquid compounds reduces the tendency of the burden to cluster excessively near the burden stockline. In this prereduction zone, the oxide feed material is reduced to low metallization, i.e. metallization less than 25%, by reaction with reductants H₂ and CO in the upwardly moving gases. Thus the burden becomes electrically conductive before it leaves the prereduction zone.

The central region of the shaft furnace constitutes a reduction zone in which metallic iron is formed by reaction of the char formed from the carbonaceous fuel with oxygen from the iron oxide. The reaction in the reduction zone are endothermic. The required heat in the reduction zone is supplied electro-thermally.

The lower region of the furnace constitutes a cooling zone wherein cold process gas or other cooling gas is passed through the hot product prior to discharge. Cold process gas enters the cooling zone through inlet 40 as in FIGS. 1 or 2, or a cooling gas circuit recirculation gas through the cooling zone between inlet 100 and outlet 110 of FIG. 3.

The product discharge from the shaft furnace contains reduced iron, ash from the coal and some residual char having very small particle size. The discharge product is screened to separate the reduced pellets, then the screen undersize is passed through a magnetic separator to recover the reduced product fines.

A small amount, up to 5 weight percent, of limestone or dolomite may be added to the feed material to react with sulfur which may be liberated within the furnace. This nonmetallic material will be rejected from the direct reduced iron product by magnetic separator.

As a specific example of the operation of each of the furnaces in FIGS. 1 through 4 calculations have been made regarding the gas flow rates, gas temperatures and gas compositions at a number of locations in each furnace flow diagram. These calculations have been based on an oxide feed analysis of 97% Fe₂ O₃, with 3% gangue materials. Ten percent more coal than is theoretically required, having a proximate analysis of 57.6% fixed carbon, 3.3% water, 29.0% volatiles and 10.1% ash was used as a basis for these calculations. This is a high volatile grade A bituminous coal. The tar and oil yield from the coal is about 0.11 cubic meters per metric ton. Tars and oil present in the top gas are 22,000 milligrams per normal cubic meter. The temperature in the reducing zone is 980° C. The metallization of the ultimate product is 92% with the metallization taking place in the prereduction zone being 20%. The use of excess coal will result in unreacted char discharging from the furnace with the metallic iron product. This char can be magnetically separated from the iron product and separated from ash by flotation or other suitable means. The resultant char can be recycled into the furnace which will reduce the coal requirement substantially to theoretical.

Tables 1 through 3 show computed operating figures for a direct reduction furnace operated in accordance with the invention. The gas analyses are typical operating figures at the locations indicated by the letter headings. These locations are as follows:

A. Top gas upon exit from top gas outlet 44.

B. Gas exiting water-scrubber 60.

C. Gas passing through vent V or V₁.

D. Gas entering furnace through inlet 72.

E. Gas entering furnace inlet 40.

F. Gas being admitted to burner 90 through line 88.

G. Cooling gas removed from cooling zone through outlet 110.

H. Cooling gas introduced to cooling zone through inlet 100.

Gas flows in the tables are given in normal cubic meters per metric ton (Nm³ /t) of Product.

Table I shows the operating figures for a direct reduction furnace being operated in accordance with either FIG. 1 or FIG. 4.

                                      TABLE 1                                      __________________________________________________________________________                                 Gas Into                                                                             Gas Out of                                                               Reduction                                                                            Reduction                                              A    B    C   E   Zone  Zone                                         __________________________________________________________________________     Flow-(Nm.sup.3 /t Prod.)                                                                 1300 1260 500 760 760   1280                                         Temp. -° C                                                                        360  40   40  40  640   980                                          Analysis - %CO                                                                           49.1 50.7 50.7                                                                               50.7                                                                               53.9  65.6                                         %CO.sub.2 23.3 24.1 24.1                                                                               24.1                                                                               20.9  8.3                                          %H.sub.2  17.0 17.6 17.6                                                                               17.6                                                                               14.4  21.0                                         %H.sub.2 O                                                                               9.0  6.0  6.0 6.0 9.2   4.5                                          %CH.sub.4 0.9  0.9  0.9 0.9 0.9   0.0                                          %N.sub.2  0.7  0.7  0.7 0.7 0.7   0.6                                          __________________________________________________________________________

Table II shows operating figures for a direct reduction furnace according to the invention being operated with the apparatus depicted in FIG. 2.

                                      TABLE II                                     __________________________________________________________________________                                      Gas Into                                                                             Gas Out of                                                               Reduction                                                                            Reduction                                       A    B    C   D   E   F  Zone  Zone                                    __________________________________________________________________________     Flow -(Nm.sup.3 /t                                                             Prod.)  1300 1260 490 35    725                                                                              10 760   1280                                    Temp. -° C                                                                      360  40   40  980   40                                                                               40 680   980                                     Analysis -%CO                                                                          49.1 50.7 50.7                                                                               53.9  50.7                                                                             50.7                                                                              53.9  65.6                                    %CO.sub.2                                                                              23.3 24.1 24.1                                                                               20.9  24.1                                                                             24.1                                                                              20.9  8.3                                     %H.sub.2                                                                               17.0 17.6 17.6                                                                               14.4  17.6                                                                             17.6                                                                              14.4  21.0                                    %H.sub.2 O                                                                             9.0  6.0  6.0 9.2   6.0                                                                              6.0                                                                               9.2   4.5                                     %CH.sub.4                                                                              0.9  0.9  0.9 0.9   0.9                                                                              0.9                                                                               0.9   0.0                                     %N.sub.2                                                                               0.7  0.7  0.7 0.7   0.7                                                                              0.7                                                                               0.7   0.6                                     __________________________________________________________________________

Table III shows operating figures for a direct reduction furnace being operated in accordance with the invention with the apparatus depicted in FIG. 3.

                                      TABLE III                                    __________________________________________________________________________                                           Gas Gas                                                                        Into                                                                               Out of                                                                     Reduc-                                                                             Reduc-                                                                     tion                                                                               tion                                         A    B    C   D   F   G   H   Zone                                                                               Zone                                 __________________________________________________________________________     Flow-(Nm.sup.3 /t                                                              Prod.)  1300 1260 260 760 240 725 725 760 1280                                 Temp. -° C                                                                      360  40   40  980 40  660 40  980 980                                  Analysis %CO                                                                           49.1 50.7 50.7                                                                               53.9                                                                               50.7        53.9                                                                               65.6                                 %CO.sub.2                                                                              23.3 24.1 24.1                                                                               20.9                                                                               24.1        20.9                                                                               8.3                                  %H.sub.2                                                                               17.0 17.6 17.6                                                                               14.4                                                                               17.6        14.4                                                                               21.0                                 %H.sub.2 O                                                                             9.0  6.0  6.0 9.2 6.0         9.2 4.5                                  %CH.sub.4                                                                              0.9  0.9  0.9 0.9 0.9         0.9 0.0                                  %N.sub.2                                                                               0.7  0.7  0.7 0.7 0.7         0.7 0.6                                  __________________________________________________________________________

The energy required to operate the furnaces of FIGS. 1, 2 and 3 are shown in Table IV.

                  TABLE IV                                                         ______________________________________                                         ENERGY REQUIREMENTS                                                                      Coal - Gcal/t                                                                             Power - kWh/t                                             ______________________________________                                         Figure 1 Furnace                                                                           2.17         826                                                   Figure 2 Furnace                                                                           2.17         811                                                   Figure 3 Furnace                                                                           2.17         700                                                   ______________________________________                                    

Note that the power requirements for the furnace of FIGS. 1 and 2 are substantially equal and for the furnace of FIG. 3 which is slightly more efficient, it is slightly less.

Tests were conducted to determine the electrical resistance of nominal 12 mm diameter metallized pellets having varying degrees of metallization. Table V is a tabulation taken from a plot of the results of these tests:

                  TABLE V                                                          ______________________________________                                         Degree of        Resistance in                                                 Metallization    Ohms per Pellet                                               ______________________________________                                         10%              0.19                                                          25%              0.14                                                          50%              0.06                                                          75%               0.025                                                        95%              0.02                                                          ______________________________________                                    

Tests have also been conducted to determine the electrical resistance at various temperatures of a packed bed burden consisting of 89% nominal 12 mm diameter pellets of approximately 90% metallization, 10% nominal 12 mm diameter coal char from low volatile bituminous coal and 1% limestone of nominal 6 mm diameter. In Table VI the resistivity represents the resistance through a burden having a face area one meter square and a resistance path depth of one meter. The table represents points taken from a curve of plotted data points:

                  TABLE VI                                                         ______________________________________                                                          Resistivity in                                                Temperature      Ohm-Meters                                                    ______________________________________                                         100° C    .0055                                                         300° C    .0033                                                         500° C    .0020                                                         700° C    .0012                                                         900° C    .0007                                                         ______________________________________                                    

The preferred reduction temperature in the furnace of the present invention is in the range of 900 to 1000° C. The burden resistivity in this temperature range at either low or high metallization requires relatively high current at relatively low voltage which makes practical the resistance heating of the burden without need for sophisticated electrical insulation or grounding means.

SUMMARY OF THE ACHIEVENTS OF THE OBJECTS OF THE INVENTION

It is clear from the above that we have invented a method and apparatus for directly reducing iron oxide to metallic iron in a shaft type reduction furnace utilizing solid fuel as the reductant source in which energy input requirements are greatly reduced over present commercial direct reduction plants and with more efficient operation than was heretofore possible.

It is to be understood that the foregoing description and specific examples are illustrative of the principles of the invention and that various modifications and additions may be made thereto by those skilled in the art without departing from the spirit and scope of the invention as set forth in the following claims: 

What is claimed is:
 1. Apparatus for reducing particulate iron oxide to metallic iron with a solid reductant, said apparatus comprising:(a) a shaft furnace having a particle introducing means generally at the top thereof and a reduced particle removal means at the bottom thereof for establishing a gravitationally descending burden therein; (b) means for passing an electric current through said burden comprising an external source of electric power, an electrode positioned substantially horizontally through said burden near the bottom of said furnace, and a second electrode positioned substantially horizontally through said burden near the top of said furnace, said electrodes being journaled for rotation; (c) a gas outlet in the upper region of said furnace for removing top gas; (d) means external to said furnace for cooling and cleaning removed top gas, said cooling and cleaning means communicating with said means for removing top gas; and (e) means communicating with said top gas cooling and cleaning means and with the interior of said furnace for returning cooled and cleaned top gas to said furnace in the lower region thereof.
 2. Apparatus according to claim 1 wherein said electrodes are connected to oscillatable drive means.
 3. Apparatus according to claim 1 further comprising at least one heat resistant alloy disc carried by each electrode.
 4. Apparatus according to claim 3 wherein said electrode disc has teeth on its outer perihery whereby it is capable of acting as a cluster breaker.
 5. Apparatus according to claim 4 wherein said electrode disc is a radially extending breaker segment extending from about 180 to about 270° about the electrode.
 6. Apparatus according to claim 1 wherein said second electrode is substantially parallel with said first electrode.
 7. Apparatus according to claim 1 further comprising means for sensing the burden temperature.
 8. Apparatus according to claim 1 further comprising means for venting excess cleaned and cooled top gas.
 9. Apparatus according to claim 1 further comprising means for heating said cooled top gas and means communicating with said heating means for introducing heated gas into the bottom of said furnace.
 10. Apparatus according to claim 1 wherein said furnace has an upper prereducing zone, a central reducing zone and a lower discharge zone, said apparatus further comprising a cooling zone between said reducing zone and said lower discharge zone, and a cooling recirculating circuit including means for introducing cooling gas into the bottom of said cooling zone, and means external to said furnace for cooling said removed cooling gas and means for recirculating cooled cooling gas to said furnace.
 11. Apparatus according to claim 10 further comprising means in said circuit external to said furnace for cleaning cooling gas.
 12. Apparatus for reducing particulate iron oxide to metallic iron with a solid reductant, said apparatus comprising:(a) a shaft furnace having a particle introducing means generally at the top thereof and a reduced particle removal means at the bottom thereof for establishing a gravitationally descending burden therein; (b) means for passing an electric current through said burden, including an external source of electric power; (c) a gas outlet in the upper region of said furnace for removing top gas; (d) means external to said furnace for cooling said removed top gas and a top gas scrubber having sludge collecting means for cleaning removed top gas, said cooling and cleaing means communicating with said gas outlet; (e) means communicating with said top gas cooling and cleaning means and with the interior of said furnace for returning cooled and cleaned top gas to said furnace in the lower region thereof; and (f) a sludge return line communicating with said scrubber and terminating in said furnace beneath the burden stockline for returning scrubber sludge to the interior of said furnace beneath the stockline.
 13. Apparatus according to claim 12 wherein said scrubber is an oil scrubber.
 14. Apparatus according to claim 12 wherein said means for cooling spent top gas is a water scrubber.
 15. Apparatus according to claim 12 further comprising means for injecting cooled cleaned top gas into said sludge return line to assist in injecting the sludge into said shaft furnace.
 16. Apparatus according to claim 12 wherein said means for passing electric current through said burden comprises horizontally opposed electrodes positioned in the walls of said furnace.
 17. Apparatus according to claim 12 wherein said means for passing electric current through said burden comprises a first electrode positioned substantially horizontally through said burden near the bottom of said furnace and a second electrode positioned substantially horizontally through said burden near the top of said furnace. 